Bazı Odun Türlerinde Bitki Ekstrakt Boyasının Eğilme Direnci/Elastiklik Modülüne Etkisi

Özet

This study was designed to develop an environmentally friendly wood stain derived . The tea plant extract is obtained in compliance with ISO
1574 -TS 1563 and impregnated in compliance with ASTM D 1413-76. For this purpose, developed the tea dye and waterborne varnish were
applied on the wood surfaces such as pine and east beech wood bending strength-elastic modules changes values are calculated. According
to experimental results, the highest value of bending strength change tea dye + AlSO4+water based varnish (79.61 N/mm2) pine wood is
obtained, at least the value of bending strength change control sample (68.23 N/mm2) was pine wood.